耐低温冲击PC EXL9414 SABIC PC
SABIC PC EXL9414 共聚物 无卤阻燃 耐低温冲击PC 充电器外壳应用
聚碳酸酯
SABIC Innovative Plastics Asia Pacific
产品说明：
LEXAN EXL9414T resin grade is a halogen-free flame retardantpolycarbonate featuring transparency, -40 degree C ductility andUL-94 V0 rating for injection molding applications. Excellentimpact combined with good flow, all transparent colorability foraesthetics and thin wall flame retradancy makes this product anexcellent candidate for thin wall applications.
LEXAN? EXL9414T resin 物性表
| 基本信息 | |
|---|---|
| 特性 |
|
| 用途 |
|
| RoHS 合规性 |
|
| 外观 |
|
| 加工方法 |
|
| 物理性能 | 额定值 | 单位制 | 测试方法 |
|---|---|---|---|
| 比重 | 1.19 | g/cm3 | ASTM D792, ISO 1183 |
| 熔流率（熔体流动速率）(300°C/1.2 kg) | 13 | g/10 min | ASTM D1238 |
| 溶化体积流率（MVR）(300°C/1.2 kg) | 12.0 | cm3/10min | ISO 1133 |
| 收缩率 - 流动(3.20 mm) | 0.40 到 0.80 | % | 内部方法 |
| 吸水率 | ISO 62 | ||
| 饱和, 23°C | 0.12 | % | ISO 62 |
| 平衡, 23°C, 50% RH | 0.090 | % | ISO 62 |