韩国SK TPEE G155D

韩国SK TPEEG155D--SKYPEL是一种热塑性聚酯弹性体（TPEE）。它是一种聚合物树脂，其性能介于塑料和橡胶之间，具有从高硬度塑料到低硬度橡胶的各种性能。它是一种热塑性弹性体，可与普通塑料模具在高温下塑化成型。

SK Chemicals提供的信息

G155D 物性表

物理性能 额定值 单位 测试方法

比重 1.18 g/cm³ ASTM D792

熔流率 (220℃/2.16 kg) 8.0 g/10 min ASTM D1238

收缩率 (流动) 1.2 % ASTM D955

吸水率 (24hr) 0.50 % ASTM D570

硬度计硬度 (邵氏 D) 55 ASTM D2240

机械性能 额定值 单位 测试方法

抗张强度 (断裂) 38.2 MPa ASTM D638

    (5.0% 应变) 7.35 MPa ASTM D638

    (10% 应变) 12.3 MPa ASTM D638

伸长率 (断裂) 550 ASTM D638

弯曲模量 2.6 MPa ASTM D790

悬臂梁缺口冲击强度 无断裂 ASTM D256

热性能 额定值 单位 测试方法

熔融温度 202 ℃

韩国SK TPEE G155D--The development of thermoplastic elastomermaterials is relatively late, so its output is not particularlylarge. However, because the output of thermoplastic materials suchas PVC is very large, and it is also relatively low, it occupies agreat advantage. More importantly, it is difficult to burn. It hasgood corrosion resistance for materials with various chemicalproperties, Therefore, the research on TPEE elastomer materials hasincreasingly attracted the attention of researchers at home andabroad. At present, the United States has a position in the R& D and production of TPEE elastomer materials in theworld. It can be said that it is the main producer and consumer ofTPEE materials in the world. TPEE thermoplastic elastomer hasexcellent thermal stability, plastic under normal operatingconditions and will not produce toxic gas, Without plasticizers andalmost no additives, problems such as viscosity changes are reducedto a certain extent. Tpc-et elastomers are hygroscopic (like allpolyesters), and will absorb moisture in the air if exposed. Thetemperature is much higher than the melting point. Excessive water(all moisture is greater than 0.1%) causes the hydrolyticdegradation of the polymer. This degradation will not show asvisual defects, but lead to poor physical properties, brittlenessand poor performance. Especially at low temperature, low-density orhigh-density polyethylene resin can be used to clean TPEEelastomer.