PA66 美国首诺 20NSP NC 耐老化

PA66 美国首诺 20NSP NC 耐老化

PA66美国首诺20NSP NC 产品信息：

物理性能额定值 (公制)额定值 (英制)测试方法比重1.14 g/cc1.14 g/ccISO 1183吸水率1.2 %1.2 %24hrs; ISO 62平衡吸湿2.4 %2.4 %Equilibrium at 50%rh; ISO 62线性成型收缩率0.014cm/cm

@Thickness 2.00 mm

0.014 in/in

@Thickness 0.0787 in

ISO 294-4线性成型收缩率，横向0.016 cm/cm

@Thickness 2.00 mm

0.016 in/in

@Thickness 0.0787 in

ISO 294-4

Ascend Performance Materials Vydyne? 20NSP Nylon 66, DAM 物性表

机械性能额定值 (公制)额定值 (英制)测试方法抗张强度(断裂)75.0 MPa10900 psiISO527-2抗张强度(屈服)98.0 MPa14200 psiISO 527-2伸长率 (断裂)13 %13 %ISO527-2屈服伸长率4.5 %4.5 %ISO 527-2拉伸模量3.80 GPa551 ksiISO 527-2弯曲强度100MPa14500 psiISO 178弯曲模量3.20 GPa464 ksiISO 178泊松比0.400.40ISO527-2悬壁梁缺口冲击强度6.00 kJ/m22.86 ft-lb/in2ISO 180
5.00 kJ/m2

@Temperature -30.0 °C

2.38 ft-lb/in2

@Temperature -22.0 °F

ISO 180简支梁无缺口冲击强度NB

@Temperature 23.0 °C

NB

@Temperature 73.4 °F

ISO 179/1eU
NB

@Temperature -30.0 °C

NB

@Temperature -22.0 °F

ISO 179/1eU简支梁缺口冲击强度0.500 J/cm2

@Temperature -30.0 °C

ISO 179/1eA
0.600 J/cm2

@Temperature 23.0 °C

2.86 ft-lb/in2

@Temperature 73.4 °F

ISO 179/1eA电气性能额定值 (公制)额定值 (英制)测试方法体积电阻率1.00e 10 ohm-cm

@Thickness 0.750 mm

1.00e 10 ohm-cm

@Thickness 0.0295 in

IEC 60093介电强度26.0 kV/mm

@Thickness 1.00 mm

660 kV/in

@Thickness 0.0394 in

IEC 60243耐电弧性120 - 179 sec

@Thickness 3.00 mm

120 - 179 sec

@Thickness 0.118 in

ASTM D495相比耐漏电起痕指数(CTI)600 V

@Thickness 3.00 mm

600 V

@Thickness 0.118 in

IEC 60112热丝引燃 (HWI)7.0 - 14 sec

@Thickness 0.710 mm

7.0 - 14 sec

@Thickness 0.0280 in

UL 746
15 - 29 sec

@Thickness 1.50 mm

15 - 29 sec

@Thickness 0.0591 in

UL 746
15 - 29 sec

@Thickness 3.00 mm

15 - 29 sec

@Thickness 0.118 in

UL 746高电弧燃烧指数(HAI)>= 120 arcs

@Thickness 0.710 mm

>= 120 arcs

@Thickness 0.0280 in

UL 746
>= 120 arcs

@Thickness 1.50 mm

>= 120 arcs

@Thickness 0.0591 in

UL 746
>= 120 arcs

@Thickness 3.00 mm

>= 120 arcs

@Thickness 0.118 in

UL 746高压电弧跟踪率，HVTR0.000 - 10.0 mm/min0.000 - 0.394 in/minUL746热性能额定值 (公制)额定值 (英制)测试方法线性热膨胀系数10.0 μm/m-°C

@Thickness 2.00 mm, Temperature 23.0 - 55.0 °C

5.56 μin/in-°F

@Thickness 0.0787 in, Temperature 73.4 - 131 °F

ISO 11359-2线性热膨胀系数,横向流动10.0 μm/m-°C

@Thickness 2.00 mm, Temperature 23.0 - 55.0 °C

ISO 11359-2熔融温度260 °C500 °FISO 11359-2载荷下热变形温度(0.46 MPa)230 °C446°FUnannealed; ISO 75-2/B载荷下热变形温度(1.8 MPa)90.0 °C194 °FUnannealed;ISO 75-2/AUL RTI130 °C

@Thickness 0.400 mm

266 °F

@Thickness 0.0157 in

UL 746
130 °C

@Thickness 0.710 mm

266 °F

@Thickness 0.0280 in

UL 746
130 °C

@Thickness 1.50 mm

266 °F

@Thickness 0.0591 in

UL 746
130 °C

@Thickness 3.00 mm

266 °F

@Thickness 0.118 in

UL 746UL RTI，机械冲击75.0 °C

@Thickness 0.400 mm

167 °F

@Thickness 0.0157 in

UL 746
75.0 °C

@Thickness 0.710 mm

167 °F

@Thickness 0.0280 in

UL 746
75.0 °C

@Thickness 1.50 mm

167 °F

@Thickness 0.0591 in

UL 746
75.0 °C

@Thickness 3.00 mm

167 °F

@Thickness 0.118 in

UL 746UL RTI，机械无冲击75.0 °C

@Thickness 0.400 mm

UL 746
85.0 °C

@Thickness 0.710 mm

185 °F

@Thickness 0.0280 in

UL 746
85.0 °C

@Thickness 1.50 mm

185 °F

@Thickness 0.0591 in

UL 746
85.0 °C

@Thickness 3.00 mm

185 °F

@Thickness 0.118 in

UL 746可燃性(UL94)V-2

@Thickness 0.400 mm

V-2

@Thickness 0.0157 in

V-2

@Thickness 0.710 mm

V-2

@Thickness 0.0280 in

V-2

@Thickness 1.50 mm

V-2

@Thickness 0.0591 in

V-2

@Thickness 3.00 mm

V-2

@Thickness 0.118 in

极限氧指数26 %26 %ISO 4589-2灼热丝易燃指数700 °C

@Thickness 0.710 mm

1290 °F

@Thickness 0.0280 in

Ignition Temp; IEC 60695-2-12
700 °C

@Thickness 1.50 mm

1290 °F

@Thickness 0.0591 in

Ignition Temp; IEC 60695-2-12
700 °C

@Thickness 3.00 mm

1290 °F

@Thickness 0.118 in

Ignition Temp; IEC 60695-2-12
800 °C

@Thickness 0.710 mm

1470 °F

@Thickness 0.0280 in

Flammability Index; IEC 60695-2-12
800 °C

@Thickness 1.50 mm

1470 °F

@Thickness 0.0591 in

Flammability Index; IEC 60695-2-12
930 °C

@Thickness 3.00 mm

1710 °F

@Thickness 0.118 in

Flammability Index; IEC 60695-2-12加工性能额定值 (公制)额定值 (英制)测试方法加工温度285 -300 °C545 - 572 °FMelt料筒后部温度260 - 280 °C500 - 536 °F
料筒中部温度270 - 285 °C518 - 545 °F
料筒前部温度280 - 290 °C536 - 554 °F
射嘴温度280 - 300 °C536 - 572 °F
模具温度65.0 - 95.0 °C149 - 203 °F
干燥温度<= 70.0 °C<= 158 °F

美国首诺PA66PA66（聚酰胺66或尼龙66），同PA6相比，PA66*广泛应用于汽车工业、仪器壳体以及其它需要有抗冲击性和 具有优良的性、自润滑性，机械强度较高。但吸水性较大，因而尺寸稳定性较差。21SPC，21X-NC，220HSP，22C，22HSP，41H，50BWFS，909，EC0315，M344，R513，R513H，R5350，Q395，R 800，52HSP，53HSP，55HSP PA66用途： 1、汽车制造方面：用于制造燃料滤网、燃料过滤器、罐、捕集器、储油槽、发动机汽缸罩、散热器水缸、平衡旋转轴齿轮。也可用在等。另外，它还可用作驱动、控制部件等。 2、电器电子工业：可用于制造电饭锅、电动吸尘器、高频电子食品加热器，电器产品的接线柱、开关和电阻器等。 3、医疗器械及精密仪器：用于医用输血管、取血器、输液器等。PA单丝可做外科手术缝线、假发等；另外，电子打字机的数字旋转盘、接线 式过滤片等。 4、其它方面：用于制作一次性打火机体、碱性干电池衬垫，摩托车驾驶员的头盔，办公机器外壳，办公用椅的角轮、座和靠背，