美国LNP 抗静电PMMA 树脂 LNP Stat-Loy 9X05426C
特点：LNP*Stat-loy* PMMA 9X05426C 是一个含有防静电的复合PMMA树脂，这种材料的新增功能包括：抗静电剂。
LNPSTAT-LOY PMMA 9X05426C
LNP™STAT-LOY™ Compound PMMA 9X05426C
Alsoknown as:LNP™ Stat-loy™ Compound PDX-05426 CCS BL5-343-2 TP Productreorder name:9X05426C
LNP*Stat-loy* 9X05426C is a compound based on PMMA resin containingAnti-Static. Added features of this material include:Antistat.
Property
TYPICALPROPERTIES(1)
MECHANICAL | Value | Unit | Standard | ||||
TensileStress,yield | 430 | kgf/cm² | ASTMD 638 | ||||
TensileStress,break | 410 | ||||||
TensileStrain,yield | 6.7 | % | |||||
TensileStrain,break | 18.4 | ||||||
TensileModulus,50mm/min | 17800 | ||||||
FlexuralStress | 560 | ASTMD 790 | |||||
FlexuralModulus | 16900 | 42 | MPa | ISO527 | 39 | 6.2 | 20.3 |
TensileModulus,1mm/min | 1470 | 44 | ISO178 | 1410 | |||
IMPACT | |||||||
IzodImpact,unnotched,23℃ | 54 | cm-kgf/cm | ASTMD 4812 | ||||
IzodImpact,notched,23℃ | 3 | ASTMD 256 | |||||
InstrumentedImpact Energy @ peak,23℃ | 29 | cm-kgf | ASTMD 3763 | ||||
MultiaxialImpact | 7 | ISO6603 | |||||
IzodImpact,unnotched 80*10*4 +23℃ | 45 | kJ/m² | ISO180/1U | ||||
IzodImpact,notched 80*10*4 +23℃ | 4 | ISO180/1A | |||||
THERMAL | |||||||
HDT,0.45MPa,3.2mm,unannealed | 79 | ℃ | ASTMD 648 | ||||
HDT,1.82MPa,3.2mm,unannealed | 67 | ||||||
CTE,-40℃to40℃,flow | 1.01E-04 | 1/℃ | ASTME 831 | ||||
CTE,-40℃to40℃,xflow | 1.08E-04 | ISO11359-2 | 1.09E-04 | ||||
HDT/Bf,0.45MPa Flatw 80*10*4 sp=64mm | ISO75/Bf | ||||||
HDT/Af,1.8MPa Flatw 80*10*4 sp=64mm | 70 | ISO75/Af | |||||
PHYSICAL | |||||||
Density | 1.14 | g/cm³ | ASTMD 792 | ||||
MoldShrinkage,flow,24 hrs(5) | 0.8 | ASTMD 955 | |||||
MoldShrinkage,xflow,24 hrs(5) | 1 | 0.82 | ISO294 | 0.98 | 1.13 | ISO1183 | |
ELECTRICAL | |||||||
VolumeResistivity | 1.E+09-1.E+11 | Ohm-cm | ASTMD 257 | ||||
SurfaceResistivity | Ohm | ||||||
SourceGMD,last updated:2007/02/27 | |||||||
ParameterInjection Molding | Value | Unit |
DryingTemperature | 75-90 | ℃ |
DryingTime | 4 | hrs |
MaximumMoisture Content | 0.01 | % |
NozzleTemperature | 215-240 | |
Front-Zone3 Temperature | ||
Middle-Zone2 Temperature | ||
Rear-Zone1 Temperature | ||
MoldTemperature | 25-90 | |
SourceGMD,last updated:2015/02/27 | ||
防静电的复合PMMA树脂，美国LNP， PMMA树脂 ，9X05426C，抗静电PMMA
PMMA_聚甲基丙烯酸甲酯，商品名ACRYREX®，高透明工程塑料，主要成分是甲基丙烯酸甲酯(MMA)，模塑料，具有良好的耐候性与耐热性，极高透明度，高光泽度，耐热，耐高温，机械性强韧，稳定的物理、化学、光学与电学特性。溶于有机溶剂，如苯酚，苯甲醚。广泛用于电子面板、机械零件、钟表外壳、指示灯外壳、电讯器材、绝缘零件、太阳眼镜，押出板、棒、管等。