塑料POM KX98009 玻纤 不锈钢纤维 增强 POM KX98009
SABICInnovative Plastics LNP FARADEX KX98009 Acetal Copolymer(Europe-Africa-Middle East)
Polymer,Thermoplastic,Acetal (POM),Acetal Copolymer, SteelFilled
SABIC Innovative Plastics (GE Plastics)
产品说明:
LNP* FARADEX* KX98009 is a compound based on Acetal Copolymerresin containing Stainless Steel Fiber, Glass Fiber. Added featuresinclude : EMI / RFI Shielding, Electrically Conductive.
SABIC Innovative Plastics LNP FARADEX KX98009 Acetal Copolymer(Europe-Africa-Middle East) 物性表
物理性能 | 额定值 (公制) | 额定值 (英制) | 测试方法 |
---|---|---|---|
密度 | 1.68 g/cc | 0.0607 lb/in³ | ISO 1183 |
吸水率 | 0.54 % @Time 86400 sec | 0.54 % @Time 24.0 hour | ISO 62-1 |
线性成型收缩率,Flow | 0.0040 cm/cm | 0.0040 in/in | SABIC Method |
机械性能 | 额定值 (公制) | 额定值 (英制) | 测试方法 |
---|---|---|---|
抗张强度(断裂) | 82.0 MPa | 11900 psi | 5 mm/min; ISO 527 |
抗张强度(屈服) | 82.0 MPa | 11900 psi | 5 mm/min; ISO 527 |
伸长率 (断裂) | 1.4 % | 1.4 % | 5 mm/min; ISO 527 |
2.2 % | 2.2 % | Flexural Strain, break, 2 mm/min; ISO 178 | |
屈服伸长率 | 1.4 % | 1.4 % | 5 mm/min; ISO 527 |
拉伸模量 | 7.90 GPa | 1150 ksi | 1 mm/min; ISO 527 |
弯曲强度 | 103 MPa | 14900 psi | 2 mm/min; ISO 178 |
116 MPa | 16800 psi | 2 mm/min; ISO 178 | |
弯曲模量 | 8.20 GPa | 1190 ksi | 2 mm/min; ISO 178 |
悬壁梁缺口冲击强度 | 6.00 kJ/m² | 2.86 ft-lb/in² | 80*10*4; ISO 180/1A |
悬壁梁无缺口冲击强度 | 20.0 kJ/m² | 9.52 ft-lb/in² | 80*10*4; ISO 180/1U |
电气性能 | 额定值 (公制) | 额定值 (英制) | 测试方法 |
---|---|---|---|
表面电阻 | 100 - 10000 ohm | 100 - 10000 ohm | ASTM D257 |
热性能 | 额定值 (公制) | 额定值 (英制) | 测试方法 |
---|---|---|---|
载荷下热变形温度(1.8 MPa) | 159 °C | 318 °F |
塑料POM, KX98009 玻纤 , 增强POM 新料,pom材料性能,pom原材料价格