C645NK 物性表
| 能 | 吸水率 | 23 ℃，24hr | ASTM D-570 | 0.2(2.8) | % |
| 模具收缩率 | 2mmt | ASTM D-955 | 0.3(0.7) | % | |
| 比重 | ASTM D-792 | 1.75 | |||
| 机械性能 | 弯曲强度 | dry(moist) | ASTM D-790 | 280(240) | MPa |
| 洛氏硬度 | ASTM D-785 | 110 | Mscale | ||
| 弯曲模量 | dry(moist) | ASTM D-790 | 13000(9000) | MPa | |
| IZOD缺口冲击强度 | dry(moist) | ASTM D-256 | 75(80) | J/M | |
| 拉伸强度 | dry(moist) | ASTM D-638 | 180(150) | MPa | |
| 拉伸伸长率 | dry(moist) | ASTM D-638 | 3(3) | % | |
| 电气性能 | 体积电阻率 | dry | ASTM D-257 | 1015 | Ω.cm |
| 损耗因数 | 1016Hz,dry | ASTM D-150 | 0.011 | ||
| 介电常数 | 1016Hz,dry | ASTM D-150 | 4.0 | ||
| 介电击穿电压 | dry | ASTM D-149 | 22 | KV/mm | |
| 热性能 | 玻璃转变温度 | 74 | ℃ | ||
| 熔点 | 310 | ℃ | |||
| 线性热膨胀系数 | ASTM D-696 | 2.0(4.5) | ×10-5/℃ | ||
| 阻燃性 | UL 94 | V-0 | |||
| 负荷挠曲温度 | ASTM D-648 | 295 | ℃ | ||
| 玻璃纤维含量 | 40 |