高分子PVDF 761阿科玛----760 is a semi-crystalline high molecularweight pelletized polymer of vinylidene fluoride. It is a versatileengineering plastic with an outstanding balance of physical andchemical properties which it for high performance servicein a wide range of applications. It is a thermoplasticfluoropolymer capable of being fabricated in standard processinge The molecular weight and molecular weight distributionhave been carefully tailored to supply a grade suitable for avariety of processing re and end-use applications.
760 is suitable for the compression molding of block andextrusion of thick monofilaments and pipe.
The powder form of this resin grade is available as 761PVDF.
760是偏氟乙烯的半结晶高分子量造粒聚合物。它是一种多用途的工程塑料，具有优异的物理和化学性能平衡，使其能够在广泛的应用中提供高性能的服务。它是一种热塑性氟聚合物，可在标准加工设备中制造。分子量和分子量分布经过精心定制，以提供适合各种加工要求和zui终用途的等级。
760适用于砌块的模压成型和厚单丝、管材的挤出成型。
该树脂等级的粉末形式为761 PVDF。
761 物性表
| 基本信息 | |
|---|---|
| 形式 |
|
| 加工方法 |
|
| 物理性能 | 额定值 | 单位制 | 测试方法 |
|---|---|---|---|
| 比重 | 1.77 到 1.79 | g/cm³ | ASTM D792 |
| 硬度 | 额定值 | 单位制 | 测试方法 |
|---|---|---|---|
| 肖氏硬度 (邵氏D, 23°C) | 76 到 80 | ASTM D2240 |
| 机械性能 | 额定值 | 单位制 | 测试方法 |
|---|---|---|---|
| 抗张强度 | ASTM D638 | ||
| 屈服, 23°C | 44.8 到 55.2 | MPa | ASTM D638 |
| 断裂, 23°C | 34.5 到 55.2 | MPa | ASTM D638 |
| 伸长率 (断裂,23°C) | 20 到 100 | ASTM D638 | |
| 弯曲模量 (23°C) | 1380 到 2310 | MPa | ASTM D790 |
| 弯曲强度 (23°C) | 58.6 到 75.8 | MPa | ASTM D790 |
| 压缩强度 (23°C) | 68.9 到 103 | MPa | ASTM D695 |
| 热性能 | 额定值 | 单位制 | 测试方法 |
|---|---|---|---|
| 熔融峰值温度 | 165 到 172 | °C | ASTM D3418 |
| 电气性能 | 额定值 | 单位制 | 测试方法 |
|---|---|---|---|
| 体积电阻率 1(20°C) | 2.0E+14 | ohms·cm | ASTM D257 |
| 充模分析 | 额定值 | 单位制 | 测试方法 |
|---|---|---|---|
| 熔体粘度 (232°C, 100 sec^-1) | 2300 到 2900 | Pa·s | ASTM D3835 |