日本油墨PPS FZ-3600-R5
| 物理性能 | 比重 | ASTMD792 | 1.96 | g/cm³ | |
| 收缩率 | 流动 | ASTMD955 | 0.25 | % | |
| 横向流动 | ASTMD955 | 1.0 | % | ||
| 吸水率(23°C,24hr) | ASTMD570 | 0.020 | % | ||
| 硬度 | 洛氏硬度 | M级 | ASTMD785 | 100 | |
| R级 | ASTMD785 | 121 | |||
| 机械性能 | 拉伸模量 | ASTMD638 | 18500 | MPa | |
| 抗张强度 | ASTMD638 | 150 | MPa | ||
| 伸长率(断裂) | ASTMD638 | 1.0 | % | ||
| 弯曲模量 | ASTMD790 | 17500 | MPa | ||
| 弯曲强度 | ASTMD790 | 230 | MPa | ||
| 压缩强度 | ASTMD695 | 170 | MPa | ||
| 泊松比 | 0.34 | ||||
| 摩擦系数 | 与钢-动态 | ASTMD1894 | 0.35 | ||
| 与钢-静态 | ASTMD1894 | 0.35 | |||
| 断裂弯曲伸长率 | ASTMD790 | 1.5 | % | ||
| 冲击性能 | 悬壁梁缺口冲击强度 | ASTMD256 | 75 | J/m | |
| 无缺口悬臂梁冲击 | ASTMD256 | 320 | J/m | ||
| 热性能 | 载荷下热变形温度(1.8MPa,未退火) | ASTMD648 | 265 | °C | |
| 线形热膨胀系数 | 流动:-30到90°C | ASTMD696 | 1.7E-5 | cm/cm/°C | |
| 横向:-30到90°C | ASTMD696 | 1.7E-5 | cm/cm/°C |