PA66 CM3004-V0东丽

PA66 CM3004-V0东丽----PA66 Toray cm3004-v0 is flame retardant,halogen-free polyamide 66 (PA66) grade. It has high fluidity,excellent strength, toughness, heat resistance and friction andwear resistance. It has excellent self extinguishing property,mechanical property, excellent gas resistance, excellent chemicalresistance, oil resistance and low gasoline permeability. Injectionmolding can be used. Recommended for digital appliances, housingequipment, office automation equipment, electronic parts andgeneral components and daily necessities applications. Comply withUL 94 V-0 flame retardant rating.

 丙烯酸树脂塑胶的特性
（1）一般特性 PA的外型为全透明或不全透明奶白色或浅黄色的粉料，传导率角质层、硬实，产品表层有光泽度。 PA的吸水性较为大，酰胺基的占比越大，吸水性越高，实际为：PA6＞PA66＞PA610＞PA1010＞PA11＞PA12＞PA1212。PA归属于自熄型塑胶，点燃时有烧糊的羊毛绒或手指甲味。PA属中等水平高阻隔塑胶，高阻隔随酰胺基/亚甲基的占比扩大而提升，以PA6的隔绝实际效果。PA6的O2通过指数为25～40㎝3?㎜/㎡?d?MpaCO2通过指数为150～200㎝3?㎜/㎡?d?MpaH2O通过指数为150g?㎜/㎡?d?Mpa
（2）物理性能PA在室内温度下的抗拉强度和冲击性抗压强度都较高，但冲击性抗压强度比不上PC和POM高。随溫度和环境湿度的上升，抗拉强度骤降，而冲击性抗压强度则明显增强。玻纤提高PA的抗压强度受溫度和环境湿度危害较小。PA的耐疲惫性不错，仅次POM，玻璃纤维提高解决后还可提升50%上下。PA的抗应力松弛性较弱，不适合生产制造高精密的承受力产品，但玻璃纤维提高后可改进。PA的耐摩擦系数和抗磨损性优质，是一种的耐磨性能塑胶种类。在其中，不一样种类的摩擦因数相距并不大，隔膜真空泵润化摩擦因数仅为0.1～0.3。耐磨性能以PA1010。PA中添加二硫化钼、高纯石墨、F4及PE等可改善摩擦系数和耐磨性能。
（3）热力学特性 PA的热变形温度也不高，一般在50～75℃。用玻纤提高后可提升4倍之上，达到200℃PA的热传导指数不大，仅为0.16～0.4W/M?K。PA的热膨胀系数很大，并随晶粒大小扩大而降低。
（4）电力学特性PA在超低温和低温干燥标准下为很好的绝缘层材料，但介电强度能随溫度和环境湿度的上升而极剧恶变，并以分子结构中含酰胺基占比近于比较敏感，比如PA6而PA12小。
（5）自然环境特性PA耐溶剂可靠性优质，能耐绝大多数溶剂如醇、对二甲苯、酯及酮等，尤其是耐磨性能突显。但PA的耐酸性、碱、盐性不太好，可造成增溶，伤害的碳酸盐为氯化镁。PA可溶解苯甲酸及酚类。PA的染色牢度不太好，太阳底下抗压强度迅速降低并变脆，不能用以室外。