POM GC15,15%玻璃纤维增强
公司的特点®gc15 POM，15%玻璃纤维增强 类别：聚合物；热塑性；聚甲醛（POM）；共聚甲醛，20%玻璃纤维增强材料说明：特点是利用®gc15标称15重量%的玻璃纤维以增加刚度和强度等级的乙缩醛共聚物。
POM GC15的物性表：
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Specific Gravity | 1.54 g/cc | 1.54 g/cc | ASTM D792 | ||
| Density | 1.502 g/cc | 0.05426 lb/in³ | ISO 1183 | ||
| Water Absorption | 0.80 % | 0.80 % | ISO 62 | ||
| Moisture Absorption | 0.200 % | 0.200 % | 23°C/50%RH; ISO62 | ||
| Linear Mold Shrinkage, Flow | 0.0040 cm/cm | 0.0040 in/in | ASTM D955 | ||
| 0.0050 cm/cm | 0.0050 in/in | ISO 294-4 | |||
| Linear Mold Shrinkage, Transverse | 0.0090 cm/cm | 0.0090 in/in | ISO 294-4 | ||
| 0.018 cm/cm | 0.018 in/in | ASTM D955 | |||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Strength at Break | 91.0 MPa | 13200 psi | 5mm/min; ISO527-2/1A | ||
| Tensile Strength, Yield | 85.5 MPa | 12400 psi | ASTM D638 | ||
| Elongation at Break | 2.5 % | 2.5 % | 5mm/min; ISO527-2/1A | ||
| Tensile Modulus | 5.95 GPa | 863 ksi | 1mm/min; ISO527-2/1A | ||
| Flexural Modulus | 5.85 GPa | 848 ksi | ISO 178 | ||
| 4.96 GPa @Temperature 22.8 °C | 720 ksi @Temperature 73.0 °F | ASTM D790 | |||
| Izod Impact, Notched | 0.641 J/cm | 1.20 ft-lb/in | ASTM D256 | ||
| Izod Impact, Notched (ISO) | 5.30 kJ/m² | 2.52 ft-lb/in² | ISO 180/1A | ||
| Charpy Impact, Notched | 0.490 J/cm² | 2.33 ft-lb/in² | ISO 179/1eA | ||
| Thermal Properties | Metric | English | Comments | ||
| CTE, linear | 46.0 µm/m-°C | 25.6 µin/in-°F | ISO 11359-2 | ||
| CTE, linear, Transverse to Flow | 100 µm/m-°C | 55.6 µin/in-°F | ISO 11359-2 | ||
| Melting Point | 165 °C | 329 °F | ASTM D3418 | ||
| 166 °C | 331 °F | 10°C/min; ISO11357-1,-2,-3 | |||
| Deflection Temperature at 1.8 MPa (264 psi) | 130 °C | 266 °F | ASTM D648 | ||
| 159 °C | 318 °F | ISO 75-1, -2 | |||
| Processing Properties | Metric | English | Comments | ||
| Processing Temperature | 90.0 - 120 °C | 194 - 248 °F | Cavitytemperature | ||
| Zone 1 | 170 - 180 °C | 338 - 356 °F | |||
| Zone 2 | 180 - 190 °C | 356 - 374 °F | |||
| Zone 3 | 180 - 190 °C | 356 - 374 °F | |||
| Zone 4 | 190 - 200 °C | 374 - 392 °F | |||
| Die Temperature | 190 - 200 °C | 374 - 392 °F | |||
| Melt Temperature | 180 - 200 °C | 356 - 392 °F | |||
| Drying Temperature | 80.0 - 100 °C | 176 - 212 °F | |||
| Dry Time | 3.00 hour | 3.00 hour | |||
| Injection Pressure | 90.0 - 140 MPa | 13100 - 20300 psi | |||
| Hold Pressure | 90.0 - 140 MPa | 13100 - 20300 psi | |||
| Back Pressure | 0.500 MPa | 72.5 psi | |||
| Hot-Working Temperature | 190 - 210 °C | 374 - 410 °F | |||
| Descriptive Properties | |||||
| Injection molding | Yes | ||||
| Injection speed | slow | ||||
| Pellets | Yes | ||||
| Pre-drying | Drying is notnormally required with proper storage | ||||
| Processing conditions | ISO 9988-2 | ||||
POM 的简介
POM强度、刚度高，弹性好，减磨耐磨性好。其力学性能优异，比强度可达50.5MPa，比刚度可达2650MPa，与金属十分接近。POM的力学性能随温度变化小，共聚POM比均聚POM的变化稍大一点。
POM的冲击强度较高，但常规冲击不及ABS和PC；POM对缺口敏感，有缺口可使冲击强度下降90%之多。
POM的疲劳强度十分突出，10交变载荷作用后，疲劳强度可达35MPa，而PA和PC仅为28MPa。
POM的蠕变性与PA相似，在20℃、21MPa、3000h时仅为2.3%，而且受温度的影响很小。
POM的摩擦因数小，耐磨性好（POM>PA66>PA6>ABS>HPVC>PS>PC），极限PV值很大，自润滑性好。
POM制品对磨时，高载荷作用时易产生类似尖叫的噪声。
POM 化学性质
POM按分子链结构不同，聚甲醛可分为均聚甲醛和共聚甲醛，前者密度、结晶度、熔点都高，但是热稳定性差，加工温度窄（10度），对酸堿的稳定性略低；后者密度、结晶度、熔点较低，但热稳定性好，不易分解，加工温度宽（50度） 。
POM不足之处在于：由受强酸腐蚀，耐侯差，粘合性差，热分解与软化温度接近，限氧指数小。它们广泛用于汽车工业，电子电器，机械设备等。还可以做水、框窗、洗漱盆。
POM具有很低的摩擦系数和很好的几何稳定性，特别适合于制作齿轮和轴承。由于它还具有耐高温特性，因此还用于管道器件（管道阀门、泵壳体），草坪设备等。
POM 环境性能:
POM不耐强酸和氧化剂，对烯酸及弱酸有一定的稳定性。
POM的耐溶剂性良好，可耐烃类、醇类、醛类、醚类、汽油、润滑油及弱碱等，并可在高温下保持相当的化学稳定性。吸水性小，尺寸稳定性好。
POM的耐候性不好，长期在紫外线作用下，力学性能下降，表面发生粉化和龟裂。
应用范围
POM属结晶性塑料，熔点明显，一旦达到熔点，熔体粘度迅速下降。当温度超过一定限度或熔体受热时间过长，会引起分解。
POM具有较好的综合性能，在热塑性塑料中是坚硬的，是塑料材料中力学性能接近金属的品种之一，其抗张强度、弯曲强度、耐疲劳强度，耐磨性和电性都十分优良，可在-40度--100度之间长期使用。