现货PMMA HI-835H 耐冲击高透明亚克力
用途概述:PMMA HI835H制作各种光学镜片，如眼镜、放大镜、各种透镜以及激光扫描控制的慢转录像带等
备注说明:手感:优质的压克力材质手感圆润柔滑，并且不带汗渍、指纹印
性能项目 | 试验条件[状态] | 测试方法 | 测试数据 | 数据单位 | |
基本性能 | 吸水率 | 24h | ASTM D-570 | 0.4 | % |
物理性能 | 反射指数 | --- | ASTM D-542 | 1.49 | --- |
比重 | ASTM D-792 | 1.17 | |||
透明性 | ASTM D-1003 | 0.4-0.8 | |||
机械性能 | 拉力 | ASTM D-638 | 395 | Kg/cm | |
延伸率 | 89 | ||||
弯曲强度 | ASTM D-790 | 713 | |||
弯曲模数 | 17510 | ||||
冲击强度 | ASTM D-256 | 4.52 | kg?cm/cm | ||
洛氏硬度 | ASTM D-785 | 65 | M-Scale | ||
电气性能 | 抗体积系数 | ASTM D-257 | >15 | Ω.m | |
介电强度 | 4KV/S | ASTM D-149 | 15 | KV/mm | |
介电定数 | 60Hz | ASTM D-150 | 3.9 | ||
功率系数 | 0.04 | ||||
热 性 能 | 维卡软化点 | 1kg | ASTM D-1525 | 90 | °C |
流动指数 | ASTM D-1238 | 2.12 | g/10min | ||
模缩系数 | ASTM D995-51 | ||||
燃烧度 | 1/8",1/16" | UL94 | HB | ||
比热 | --- | 0.35 | cal/g/°C | ||
绵性膨胀系数 | ASTM D-696 | 7×10 | cm/cm/°C | ||
热传导 | ASTM D-177 | 5×10 | cal/seccm・°C/cm | ||
热变形温度 | 18.56kg | ASTM D-648 | 92 | ||