SABIC Innovative Plastics Noryl GTX GTX917 PPE+PS+PA 物性表
| 物理性能 | 额定值 (公制) | 额定值 (英制) | 测试方法 |
|---|---|---|---|
| 比重 | 1.10 g/cc | 1.10 g/cc | ASTM D 792 |
| 线性成型收缩率,Flow | 0.011 - 0.013 cm/cm @Thickness 3.20 mm | 0.011 - 0.013 in/in @Thickness 0.126 in | SABIC Method |
| 线性成型收缩率，横向 | 0.010 - 0.012 cm/cm @Thickness 3.20 mm | 0.010 - 0.012 in/in @Thickness 0.126 in | SABIC Method |
| 机械性能 | 额定值 (公制) | 额定值 (英制) | 测试方法 |
|---|---|---|---|
| 抗张强度(屈服) | 68.0 MPa | 9860 psi | Type I, 50 mm/min; ASTM D 638 |
| 伸长率 (断裂) | 40 % | 40 % | Type I, 50 mm/min; ASTM D 638 |
| 弯曲强度 | 103 MPa | 14900 psi | 2.6 mm/min, 100 mm span; ASTM D 790 |
| 弯曲模量 | 2.48 GPa | 360 ksi | 2.6 mm/min, 100 mm span; ASTM D 790 |
| 悬壁梁缺口冲击强度 | 1.86 J/cm @Temperature 23.0 °C | 3.48 ft-lb/in @Temperature 73.4 °F | ASTM D 256 |
| 冲击试验 | 27.0 J @Temperature -30.0 °C | 19.9 ft-lb @Temperature -22.0 °F | Instrumented Impact Energy @ peak; ASTM D 3763 |
| 53.0 J @Temperature 23.0 °C | 39.1 ft-lb @Temperature 73.4 °F | Instrumented Impact Energy @ peak; ASTM D 3763 |