低价PA6日本东丽CM1017 标准级耐磨损
生产工艺：注塑成型
产品优势：
性能特点 | 低温韧性耐热性，高生产阶段，快自熄 |
产品规格：25公斤/包
PA6日本东丽CM1017物性表
| PA6 CM1017 日本东丽工业株式会社物性数据 |
| 规格级别： | 注塑级 | 外观颜色： | --- |
| 用途概述： | --- | ||
| 备注说明： | 类型：尼龙-6未强化，标准等级 | ||
| 性能项目 | 试验条件[状态] | 测试方法 | 测试数据无水3.5%水 | 数据单位 | |
| 基本性能 | 吸水率 | 23℃，24小时 | ASTM D-570 | 1.8- | % |
| 物理性能 | 比重 | --- | ASTM D-792 | 1.12-1.14- | --- |
| 泰伯磨耗量 | 1000g,CS-17 | ASTM D-1044 | 3-4- | mg/1000次 | |
| 机械性能 | IZOD冲击强度 | 无缺口1/2"，23℃ | --- | 540 | kg.cm/cm |
| IZOD冲击强度 | 23℃，无缺口1/8 | --- | 无断裂- | kg.cm/cm | |
| 洛氏硬度 | 23℃ | ASTM D-785 | 11990 | --- | |
| 洛氏硬度 | 23℃ | ASTM D-785 | 83- | --- | |
| 抗拉屈服强度 | -40 | ASTM D-638 | 12301150 | Kg/cm2 | |
| 抗拉屈服强度 | 23℃ | ASTM D-638 | 820420 | Kg/cm2 | |
| 抗拉屈服强度 | 80℃ | ASTM D-638 | 320220 | Kg/cm2 | |
| 抗拉断裂强度 | 23℃ | ASTM D-638 | 20- | Kg/cm2 | |
| 断裂伸长率 | 23℃ | ASTM D-638 | 180<200 | % | |
| 挠曲强度 | -40℃ | ASTM D-790 | 15001450 | Kg/cm2 | |
| 挠曲强度 | 23℃ | ASTM D-790 | 1100450 | Kg/cm2 | |
| 挠曲强度 | 80℃ | ASTM D-790 | 500300 | Kg/cm2 | |
| 挠曲模量 | -40℃ | ASTM D-790 | 4000037000 | Kg/cm2 | |
| 挠曲模量 | 23℃ | ASTM D-790 | 2900010000 | Kg/cm2 | |
| 挠曲模量 | 80℃ | ASTM D-790 | 80004000 | Kg/cm2 | |
| 压缩强度 | 23℃ | ASTM D-695 | 890- | Kg/cm2 | |
| 搞剪强度 | 23℃ | ASTM D-732 | 740690 | Kg/cm2 | |
| IZOD冲击强度 | -40℃，无缺口1/2 | --- | 3.515 | kg.cm/cm | |
| 电气性能 | 体积电阻率 | --- | ASTM D-257 | 1014-10151011-1012 | Ω.cm |
| 介电强度 | 1/8" | ASTM D-149 | 20- | KV/mm | |
| 介电常数 | 50HZ | ASTM D-150 | 4.1- | --- | |
| 介电常数 | 106Hz | ASTM D-150 | 3.9- | --- | |
| 介电常数 | 106Hz | ASTM D-150 | 3.4- | --- | |
| 损耗因素 | 50Hz | ASTM D-150 | 50Hz- | --- | |
| 损耗因素 | 103Hz | ASTM D-150 | 0.06- | --- | |
| 损耗因素 | 106Hz | ASTM D-150 | 0.03- | --- | |
| 抗电弧性 | 1/8" | ASTM D-150 | 121- | --- | |
| IEC导电径踪指数 | --- | UL 746 | ≤600- | V | |
| 热 性 能 | 线性热膨胀系数 | --- | ASTM D-696 | 8- | 10-5cm/cm.℃ |
| 热挠曲温度 | --- | ASTM D-648 | 190- | ℃ | |
| 热挠曲温度 | 18.6kg/cm2 | ASTM D-648 | 190- | ℃ | |
| UL-94抗燃级 | --- | UL 94 | V-2(1/16")- | --- | |
| 熔点 | --- | 差示扫描测热计DSC法 | 225- | ℃ | |
| 比热 | --- | --- | 0.46- | Cal/g.°C | |
| 导热系数 | --- | --- | 0.18- | Kcal/m.hr.°C | |