Fortron® 4184L4 物性表
基本信息黄卡编号E107854-237743E107854-237744填料/增强材料 玻璃\矿物, 53% 填料按重量特性刚性，良好良好的电气性能良好的抗蠕变性耐化学性良好耐热性，高阻燃性用途 电气/电子应用领域阀门/阀门部件连接器RoHS 合规性联系制造商多点数据 Isothermal Stress vs. Strain (ISO 11403-1)
硬度额定值单位制测试方法洛氏硬度 M级 100ASTM D785 M 计秤 100ISO 2039-2 机械性能额定值单位制测试方法拉伸模量 16600MPaISO527-2/1A/1 抗张强度 断裂,23°C 165MPaASTM D638 断裂 165MPaISO 527-2/1A/5 伸长率 断裂, 23°C1.5%ASTM D638 断裂 1.4%ISO 527-2/1A/5 弯曲模量 (23°C)16200MPaISO 178 弯曲应力 1250MPaISO 178 压缩强度(1% 应变, 23°C)207MPaASTM D695冲击性能额定值单位制测试方法简支梁缺口冲击强度 ISO 179/1eA -30°C7.0kJ/m²ISO 179/1eA 23°C 7.0kJ/m²ISO 179/1eA 简支梁无缺口冲击强度 ISO 179/1eU -30°C29kJ/m²ISO 179/1eU 23°C 29kJ/m²ISO 179/1eU 悬壁梁缺口冲击强度 ISO 180/1A -30°C7.0kJ/m²ISO 180/1A 23°C 7.0kJ/m²ISO 180/1A 无缺口伊佐德冲击强度 (23°C)27kJ/m²ISO 180/1U 热性能额定值单位制测试方法载荷下热变形温度 0.45 MPa, 退火280°CASTM D648 1.8MPa, 未退火 265°CASTM D648 1.8 MPa, 未退火 270°CISO 75-2/A 8.0 MPa, 未退火215°CISO 75-2/C 玻璃转化温度 290.0°CISO 11357-2 熔融温度 3280°CISO 11357-3线形热膨胀系数 ISO 11359-2 流动 2.4E-5cm/cm/°CISO 11359-2 横向3.2E-5cm/cm/°CISO 11359-2 电气性能额定值单位制测试方法表面电阻率 > 1.0E+15ohmsIEC60093 体积电阻率 --1.0E+16ohms·cmASTM D257 -- > 1.0E+15ohms·cmIEC 60093 介电强度 --418kV/mmASTM D149 -- 27kV/mmIEC 60243-1 介电常数 1 kHz 3.80ASTMD150 1 MHz3.80ASTM D150 1MHz 4.70IEC 60250 耗散因数 60 Hz 1.0E-3ASTM D150 1 kHz1.0E-3ASTM D150 1MHz 8.0E-4ASTM D150 1 MHz 2.0E-3IEC 60250 耐电弧性 156secASTM D495 漏电起痕指数150VIEC 60112 可燃性额定值单位制测试方法UL 阻燃等级 UL 94 0.750 mm V-0UL94 1.50 mmV-0UL 94 注射额定值单位制干燥温度 130 到 140°C干燥时间 3.0 到 4.0hr建议的Zui大水分含量0.020%料斗温度 20.0 到 30.0°C料筒后部温度 290 到 300°C料筒中部温度 310 到 320°C料筒前部温度330 到 340°C射嘴温度 310 到 330°C加工（熔体）温度 330 到 340°C模具温度 140 到 160°C注塑压力50.0 到 100MPa注射速度 快速保压 30.0 到 70.0MPa背压 0.00 到 3.00MPa
PPS塑胶原料 美国菲利浦R-4XT, 玻璃纤维增强材料, 40%抗撞击性，良好延展性UL94阻燃V0,5VA
PPS塑胶原料 美国菲利浦R-402XT玻璃纤维增强材料, 40%抗撞击性，良好UL94阻燃V0,5VA
PPS美国菲利浦R-7-120：R-7-120NA：R-7-121NR：R-9-02：BR-42C：R-10-7006A：R-7-02：R-7-120BL：XK2240BL
PPS plastic raw material Japan baoli 1150A64 glass fiber glassscale, 50% UL94 flame retardant VO,PPS plastics material paoli1140T11, glass fiber reinforced impact resistance, high automotiveapplications electrical/electronic applications UL 94 flameretardant V2PPS plastic raw material Japan baoli 1140A1 glass fiberreinforced material, 40% ultra-high toughness UL94, flame retardantVOPPS plastic raw material Japan baoli 1130A6 flame retardant v-0glass fiber enhanced 30% high strengthPPS plastic raw materialpaoli 1140A6 flame retardant v-0 glass fiber enhanced 40% highstrengthPPS plastic raw material Japan baoli 6465A62packing/reinforcement material glass mineral, 60% UL94, flameretardant VOPPS plastic material: glass fiber reinforced material,30% PTFE lubricant has good abrasion resistance UL94, flameretardant VOPPS plastic material: Japan baoli 2130A1 carbon fiberreinforced material, 30% good wear resistance, conductive UL94,flame retardant VOPPS plastic materials toray A604, A604X95,A604X97super toughness glass fiber reinforced material, 40% UL94, flameretardant VOPPS plastic material Toray Resin A310MX04packing/reinforcing material glass inorganic 65%PPS plasticmaterial toray A503 glass fiber reinforced material, 30% UL94,flame retardant VOPPS plastic material torri A310M rigid, highglass, inorganic, 70% UL94, flame retardant VO. The A400MA305M,Toray A504X90 glass fiber reinforced material, 40% supertoughness and high strength UL94, flame retardant VOPPS plasticmaterial toray ar04-b glass fiber reinforced material, 40% UL94,flame retardant VOPPS plastic material toray A674M2 reinforcementmaterial, 40% impact resistance, high UL94, flame retardant VOPPSplastic material torri AR10M-B reinforced material glass \inorganic, 65% UL94, flame retardant VOPPS plastic raw materialstoray E604, A390M65, A310MX04,