产品参数
性能项目 | 试验条件[状态] | 测试方法 | 测试数据 | 数据单位 | |
物理性能 | 比重 | -- | ASTM D792 | 1.67 | g/m2; |
收缩率 | 流动(3.18 mm) | ASTM D955 | 0.30 | ||
洛氏硬度 | R 计秤 | ASTM D785 | 118 | ||
机械性能 | 抗张强度 | 断裂, -40°C | ASTM D638 | 170 | MPa |
断裂, 23°C | ASTM D638 | 135 | MPa | ||
断裂, 80°C | ASTM D638 | 82.0 | MPa | ||
断裂, 121°C | ASTM D638 | 60.0 | MPa | ||
伸长率 | 断裂, -40°C | ASTM D638 | 2.0 | ||
断裂,23°C | ASTM D638 | 2.0 | |||
断裂,80°C | ASTM D638 | 4.1 | |||
断裂,121°C | ASTM D638 | 5.7 | |||
弯曲模量 | 23°C | ASTM D790 | 9930 | MPa | |
弯曲强度 | 23°C | ASTM D790 | 215 | MPa | |
简支梁缺口冲击强度 | 23°C | ASTM D256 | 90 | J/m | |
热性能 | 热变形温度 | 1.8 MPa, 未退火 | ASTM D648 | 223 | °C |
熔融温度 | ASTM D3418 | 250 | °C | ||
电气性能 | 体积电阻率 | 1.50mm | ASTM D257 | >1.0E+13 | ohm.cm |
介电强度 2 | 1.50mm | ASTM D149 | 29 | KV/mm | |
UL 阻燃等级 | 1.50mm | UL 94 | V-0 | ||
UL746 | RTI Str | 1.50mm | UL 746 | 155 | °C |
RTI Imp | 1.50mm | UL 746 | 155 | °C | |
RTI Elec | 1.50mm | UL 746 | 155 | °C |
特点:Petra130 FR BK-112 是巴斯夫公司研发的一款含30%玻璃纤维增强,阻燃PET材料
· PET130 FR BK-112 加玻纤30%增强,阻燃V0级
Petra®PET 130 FR BK-112
30%玻璃纤维增强材料
PET
聚对苯二甲酸乙二醇酯
BASFCorporation
产品说明:
Petra130 FR BK-112 is a 30% glass fiber reinforced, black pigmented,flame retardant injection molding compound based on post-consumerand post-industrial recycle polyethylene terephthalate feedstocks.It is recognized as UL 94V-0/5VA by UnderwritersLaboratories.
Applications
Petra130 FR BK-112 is generally recommended for applications such aselectrical housing and bobbins.
黄卡下载:E36632-231235
填料增强:含30%玻璃纤维增强材料
材料特性:阻燃级
材料用途:电器外壳,线轴
加工方法:注射成型
产品颜色:黑色粒子
塑料牌号:PET130 FR BK-112