滑石填料PP TB52道达尔--TB52 is a heat-resistant polypropylene compounddesigned for use in injection molding, and features highly improvedstrength and heat resistance. TB52 is manufactured by adding aninorganic filler, talc to polypropylene, produced with a variety ofbase PPs, such as HIPP (High Isotactic or High CrystallinePolypropylene), SAC special processing technology results in thehighest This product features superior rigidity and impactstrength, long-term heat resistance and anti-static property anddimensional stability. This SAC product is widely used in electricand electronic parts, household appliances and automobiles.
TB52是一种耐热聚丙烯化合物,设计用于注塑成型,具有高度提高的强度和耐热性。TB52是通过向聚丙烯中添加无机填料滑石来制造的,使用多种基础PPs生产,如HIPP(高等规或高结晶聚丙烯),SAC特殊加工技术可获得高质量。该产品具有优越的刚性和冲击强度、长期耐热性、抗静电性和尺寸稳定性。SAC产品广泛应用于电子电器、家用电器、汽车等领域。
物理性能 | 额定值 | 单位制 | 测试方法 |
---|
密度 | 1.07 | g/cm³ | ASTM D1505 |
熔流率(熔体流动速率) (230°C/2.16 kg) | 11 | g/10 min | ASTM D1238 |
收缩率 - 流动 (2.00 mm) | 1.0 到 1.4 | % | ASTM D955 |
硬度 | 额定值 | 单位制 | 测试方法 |
---|
洛氏硬度 (R级) | 93 |
| ASTM D785 |
机械性能 | 额定值 | 单位制 | 测试方法 |
---|
抗张强度 1(屈服) | 34.3 | MPa | ASTM D638 |
伸长率 2(断裂) | 60 | % | ASTM D638 |
弯曲模量 3 | 2450 | MPa | ASTM D790 |
冲击性能 | 额定值 | 单位制 | 测试方法 |
---|
悬壁梁缺口冲击强度 (23°C) | 49 | J/m | ASTM D256 |
热性能 | 额定值 | 单位制 | 测试方法 |
---|
载荷下热变形温度 (0.45 MPa, 未退火) | 139 | °C | ASTM D648 |
注射 | 额定值 | 单位制 |
|
---|
料筒后部温度 | 180 到 200 | °C |
|
料筒中部温度 | 190 到 210 | °C |
|
料筒前部温度 | 200 到 220 | °C |
|
模具温度 | 50.0 到 80.0 | °C |
|
注塑压力 | 39.2 到 88.3 | MPa |
|
保压 | 58.8 到 98.1 | MPa |
|
螺杆转速 | 30 到 80 | rpm |
|