稳定剂的尼龙6工程塑料 PA6 SEGM35 H1 BK-126 含玻纤和矿物填料
特点:BASFUltramid PA6 SEGM35 H1 BK-126 是一款含15%玻璃纤维增强材料和含25%矿物填料,热稳定剂的尼龙6工程塑料。
PA6SEGM35 H1 BK-126 含玻纤和矿物填料
Ultramid®PA6 SEGM35 H1 BK-126
聚酰胺6
玻璃纤维增强材料,15%;矿物填料,25%
BASFCorporation
产品说明
UltramidSEGM35 H1 BK-126 is a 40% glass/mineral reinforced injectionmolding grade. It offers enhanced surface appearance, it alsoexhibits similar UV weathering characteristics compared to 8267G HSBK-106. In parts containing cross sections, significant pressuredrops are encountered during filling.
Applications
UltramidSEGM35 H1 BK-126 is generally recommended for applications such asmirror housings, rear liftgate handles and luggage rackcomponents.
含添加剂:热稳定剂
填料增强:含15%玻璃纤维增强材料和含25%矿物填料
材料特点:尺寸稳定,低粘度,刚性佳,抗紫外线,易加工,表面光洁度好,抗热老化,流动性好,耐化学,耐磨蚀
材料用途:ElectricalHousing,把手,工业领域,汽车领域的应用,汽车外部零件,外壳
外观颜色:黑色
产品形式:颗粒料
加工方法:注射成型
塑料牌号:PA6SEGM35 H1 BK-126
定属记号:尼龙6
稳定剂的尼龙6工程塑料, PA6 SEGM35 H1 BK-126, PA6 含玻纤和矿物填料
品名:聚酰胺6或尼龙6(PA6)
分子式:[-NH-(CH2)5-CO]n- ?
性状:半透明或不透明乳白色结晶形聚合物 ?
?特性:热塑性、轻质、韧性好、耐化学品和耐久性好
燃烧鉴别方法:蓝底黄火焰,烧植物味 ?
溶剂实验:耐环己酮和芳香溶剂
密度:1.13g/cm3 熔点:215℃ ?
热分解温度 gt;300℃
平衡吸水率:3.5% 具有良好的耐磨性、自润滑性和耐溶剂性。
密 度:(g/cm3) 1.14-1.15
熔 点:215-225℃ 拉伸强度 gt; 60.0Mpa 伸 长 率 gt; 30% ?
弯曲强度: 90.0Mpa 缺口冲击强度:(KJ/m2) > 5
应用范围
工业生产中泛用于制造轴承、圆齿轮、凸轮、伞齿轮、各种滚子、滑轮、泵叶轮、风扇叶片、蜗轮、推进器、螺钉、螺母、垫片、高压密封圈、耐油密封垫片、耐油容器、外壳、软管、电缆护套、剪切机滑轮套、牛头刨床滑块、电磁分配阀座、冷陈设备、衬垫、轴承保持架、汽车和拖拉机上各种输油管、活塞、绳索、传动皮带,纺织机械工业设备零雾料,以及日用品和包装薄膜等。
加工工艺。干燥处理:由于PA6很容易吸收水分,因此加工前的干燥特别要注意,如果材料是用防水材料包装供应的,则容器应保持密闭。如果湿度大于0.2%,建议在80℃以上的热空气中干燥16小时。如果材料已经在空气中暴露超过8小时,建议进行温度为105℃,8小时以上的真空烘干。
融化温度: 230-280℃,对于增强品种为250-280℃。