巴斯夫A3EG3巴斯夫A3EG3代为整理

PhysicalPropertiesMetricEnglishCommentsDensity 1.24 g/cc0.0448 lb/in³dry;ISO 1183Water Absorption 7.0 %7.0 %beginning dry; ISO62Moisture Absorption at Equilibrium 2.2 %2.2 %beginning dry(23°C/50% R.H.); ISO 62ViscosityNumber 145 cm³/g1.45 dl/gLinear MoldShrinkage 0.0055 cm/cm0.0055 in/inASTM Data; MDMeltFlow 70 g/10 min@Load 5.00 kg,Temperature 275°C70 g/10 min@Load 11.0 lb,Temperature 527 °FISO1133Mechanical PropertiesMetricEnglishCommentsTensile Strength,Ultimate 85.0 MPa12300 psi5mm/min; ISO 527Elongationat Break 10 %10 %5mm/min; ISO 527TensileModulus 4.50 GPa653 ksi1mm/min; ISO 527FlexuralStrength 125 MPa18100 psiISO DataFlexuralModulus 4.00 GPa580 ksiISO DataIzod Impact, Notched(ISO) 14.0 kJ/m²6.66 ft-lb/in²ISO TestCharpy ImpactUnnotched 7.00 J/cm²33.3 ft-lb/in²ISO 179CharpyImpact, Notched 1.10 J/cm²5.24 ft-lb/in²ISO179Tensile Creep Modulus, 1000hours 2500 MPa363000 psiISO 899ElectricalPropertiesMetricEnglishCommentsVolumeResistivity 1.00e+10 ohm-cm1.00e+10 ohm-cmIEC60093Surface Resistance 1.00e+10 ohm1.00e+10 ohmIEC60093Dielectric Constant 5.5@Frequency 1.00e+6 Hz5.5@Frequency1.00e+6 HzIEC 60250Dissipation Factor  0.16@Frequency1.00e+6 Hz0.16@Frequency 1.00e+6 HzIEC 602500.30@Frequency 100Hz0.30@Frequency 100 HzIEC 60250Comparative TrackingIndex 550 V550 VIEC 60112ThermalPropertiesMetricEnglishCommentsMeltingPoint 260 °C500 °F10 K/min260 °C500 °FASTMTestCompliance PropertiesMetricEnglishCommentsFDA YesYes21 CFR177.1500NSF YesYesNSF Std. 51DescriptivePropertiesColorNaturalCommercial StatusActiveAmericaFormPelletsImpact ModifiedNoPrimary ProcessingTechniqueInjection MoldingProcessingInjection MoldingSpecialcharacteristicHeat stabilized or stable to heat