EVA 台湾台聚 UE659 热融级
Excellent soldering resistance makes PA6T particularly suitable forsurface-mount technology electrical connector. 2. Excellent hightemperature rigidity PA6T can maintain quite high modulus at hightemperature, such as 55% of modulus
| 性能项目 | 试验条件[状态] | 测试方法 | 测试数据 | 数据单位 | ||
| 基本性能 | 熔体流动速率 | ASTM D-1238 | 2 | g/10min | ||
| 密度 | ASTM D-1505 | 0.947 | g/cm3 | |||
| 机械性能 | 硬度 | ASTM D-2240 | 31 | Shore D | ||
| 延展性 | 铸膜成型 | ASTM D-638（ASTM D-882） | 890 | % | ||
| 射出 | ASTM D-638（ASTM D-882） | 236 | % | |||
| 薄膜MD | ASTM D-638（ASTM D-882） | 290 | % | |||
| 薄膜TD | ASTM D-638（ASTM D-882） | 680 | % | |||
| 低温易脆性 | ASTM D-746 | ＜-76 | ℃/F50 | |||
| 冲击强度 | ASTM D-1709 | 444 | G/F50 | |||
| 降伏点抗张强度 | 铸膜成型 | ASTM D-638（ASTM D-882） | 212 | KG/cm2 | ||
| 射出 | ASTM D-638（ASTM D-882） | 114 | KG/cm2 | |||
| 薄膜MD | ASTM D-638（ASTM D-882） | 259 | KG/cm2 | |||
| 薄膜TD | ASTM D-638（ASTM D-882） | 240 | KG/cm2 | |||
| 热性能 | 熔点 | ASTM D-2117 | 77 | ℃ | ||
| 维卡软化点 | ASTM D-1525 | 54 | ℃ | |||
| 其它性能 | VA含量 | USIFE | 25 | % | ||
EVA 台湾台聚 UE659 热融级
Waterabsorption is low for nylon resin, the water absorption of PA6T isquite low, only 1/4 to 1/3 of Nylon 66. Therefore, the physicalproperties of PA6T are relatively small due to water absorption. 5.Excellent dimensional stability PA6T water absorption rate is verylow, because of water absorption