· 特点:LNP*STAT-LOY* POM KX95702 是一种含有防静电的化合物聚甲醛树脂,这种材料的新增功能包括:抗静电剂。
· LNPSTAT-LOY POM KX95702
LNP™STAT-LOY™ Compound POM KX95702
Alsoknown as:LNP™ Stat-loy™ Compound PDX-K-95702 Product reordername:KX95702
LNP STAT-LOY* KX95702 is a compound based on Acetal resincontaining Anti-Static. Added features of this material include:Antistat.
Property
TYPICAL PROPERTIES(1)
MECHANICAL | Value | Unit | Standard | ||||
TensileStress,yield | 410 | kgf/cm² | ASTMD 638 | ||||
TensileStress,break | 250 | ||||||
TensileStrain,yield | 18.1 | % | |||||
TensileStrain,break | 75.5 | ||||||
TensileModulus,50mm/min | 15300 | ||||||
FlexuralStress | 470 | ASTMD 790 | |||||
FlexuralModulus | 14100 | 41 | MPa | ISO527 | 31 | 14.6 | 52.4 |
TensileModulus,1mm/min | 1110 | 35 | ISO178 | 1350 | |||
IMPACT | |||||||
IzodImpact,unnotched,23℃ | NB | cm-kgf/cm | ASTMD 4812 | ||||
IzodImpact,notched,23℃ | 16 | ASTMD 256 | |||||
InstrumentedImpact Energy @ peak,23℃ | 230 | cm-kgf | ASTMD 3763 | ||||
MultiaxialImpact | 168 | ISO6603 | |||||
IzodImpact,unnotched 80*10*4 +23℃ | kJ/m² | ISO180/1U | |||||
IzodImpact,notched 80*10*4 +23℃ | 14 | ISO180/1A | |||||
THERMAL | |||||||
HDT,1.82MPa,3.2mm,unannealed | 78 | ℃ | ASTMD 648 | ||||
CTE,-40℃to40℃,flow | 1.24E-04 | 1/℃ | ASTME 831 | ||||
CTE,-40℃to40℃,xflow | 1.39E-04 | ISO11359-2 | |||||
HDT/Af,1.8MPa Flatw 80*10*4 sp=64mm | 64 | ISO75/Af | |||||
PHYSICAL | |||||||
Density | 1.32 | g/cm³ | ASTMD 792 | ||||
MoistureAbsorption,50% RH,24 hrs | 4.05 | ASTMD 570 | |||||
MoldShrinkage,flow,24 hrs(5) | 1.7 | ASTMD 955 | |||||
MoldShrinkage,xflow,24 hrs(5) | 1.8 | 1.74 | ISO294 | 1.83 | |||
ELECTRICAL | |||||||
SurfaceResistivity | 1.E+09-1.E+11 | Ohm | ASTMD 257 | ||||
SourceGMD,last updated:2004/10/01 |
ParameterInjection Molding | Value | Unit |
DryingTemperature | 80 | ℃ |
DryingTime | 4 | hrs |
MeltTemperature | 195-205 | |
Front-Zone3 Temperature | 200-210 | |
Middle-Zone2 Temperature | 190-200 | |
Rear-Zone1 Temperature | 175-190 | |
MoldTemperature | 70-95 | |
BackPressure | 0.2-0.3 | MPa |
ScrewSpeed | 30-60 | rpm |