高光泽 PMMA Hi-Gloss NTA-3 用于汽车背光源，汽车隔热封装
特点：EvonikIndustries AG Plexiglas PMMA Hi-Gloss NTA-3 用于汽车背光源，汽车隔热封装，汽车防撞杆，汽车领域的应用
PMMAHi-Gloss NTA-3 高光泽,高抗撞击,高流动
Plexiglas®PMMA Hi-Gloss NTA-3
聚甲基丙烯酸甲酯-丙烯酸
EvonikIndustries AG
产品说明
ProductProfile:
PLEXIGLAS®Hi-Gloss NTA-3 is a compound with an increased heat deflectiontemperature based on polymethyl methacrylate (PMMA).
Besidesthe well-known properties of PLEXIGLAS® molding compound, suchas
﹒goodflow
﹒highmar resistance
﹒goodweather resistance
﹒goodpolishability,
PLEXIGLAS®Hi-Gloss NTA-3 offers the added benefit of
﹒increasedheat deflection temperature under load.
Application:
PLEXIGLAS®Hi-Gloss NTA-3 is particularly suitable for injection moldingtechnical components.
Owingto its superior brilliance, high-gloss (Class A) surfaces can beobtained in opaque colors.
Examples:
automotivebody parts: window channels, pillar panels
材料特点：高光泽，高抗撞击，流动性高，耐气候影响
材料用途：AutomotiveBacklights，AutomotiveWindow Encapsulation，汽车防撞杆，汽车领域的应用，汽车外部零件，汽车外部装饰
产品外观：不透明
产品形式：颗粒料
加工方法：注射成型
定属记号：丙烯酸(PMMA)
塑料牌号：PMMAHi-Gloss NTA-3
材料物性
物理性能 | 额定值 | 单位制 | 测试方法 |
密度 | 1.18 | g/cm³ | ISO1183 |
溶化体积流率(MVR)(230℃/3.8kg) | 2.00 | cm³/10min | ISO1133 |
吸水率(23℃,24hr) | >3.0 | % | ISO62 |
机械性能 | 额定值 | 单位制 | 测试方法 |
拉伸模量 | 2900 | MPa | ISO527-2/1 |
拉伸应力(断裂) | 60.0 | ISO527-2/5 | |
拉伸应变(断裂) | 2.6 | ||
冲击性能 | |||
简支梁缺口冲击强度(23℃) | 16 | kJ/m² | ISO179/1eU |
热性能 | |||
热变形温度 | |||
0.45MPa,未退火 | 106 | ℃ | ISO75-2/B |
1.8MPa,未退火 | ISO75-2/A | ||
玻璃转化温度 | 126 | ISO11357-2 | |
维卡软化温度 | 116 | ISO306/B50 | |
可燃性 | |||
热灯丝点火温度 | 675 | IEC60695-2-13 | |
补充信息 | 测试方法 | ||
FireRating | B2 | DIN4102 | |
注射 | 额定值 | ||
干燥温度 | <100 | ||
干燥时间 | 2.0到3.0 | hr | |
加工(熔体)温度 | 220到250 | ||
模具温度 | 50.0到85.0 | ||