8231G HS 德国巴斯夫 PA6,产品说明;Ultramid 8231GHS是一种热稳定,15%玻璃纤维增强PA6注塑复合材料。它也可在非热稳定(Ultramid8231)和/或着色版本。玻璃纤维增强材料增强了材料的强度、刚度和热变形温度等性能。热稳定系统在高温下扩展了性能。它还具有优良的抗油脂、油脂和碳氢化合物的化学性能。Ultramid8231GHS是更苛刻的性能应用的理想选择,如安全帽零件,垫圈,齿轮,发动机和电机零件,滑槽,和更高的温度环境。
【PA性质】:
结晶性热可塑性塑料,有明显熔点
Nylon6 Tm为220-230℃,Nylon66则为260-270
Nylon本身具吸水基故有吸水性,成形前须干燥
温度过高干燥则尼龙粒变色。
Ultramid®8231G HS
聚酰胺6
15% 玻璃纤维增强材料
BASF Corporation
产品说明:
Ultramid8231G HS is a heat stabilized, 15% glass fiber reinforced PA6injection molding compound. It is also available in non-heatstabilized (Ultramid 8231) and/or pigmented versions. The glassfiber reinforcement enhances performance such as strength,stiffness and heat deflection temperature. The heat stabilizersystem extends the properties at elevated temperatures. It also hasexcellent chemical resistance to greases, oils andhydrocarbons.
Applications
Ultramid 8231GHS is ideally suited for more demanding performance applicationssuch as safety helmet parts, washers, gears, engine and motorparts, chutes, and higher temperature environments.
Ultramid® 8231G HS 物性表
基本信息
黄卡编号E36632-231123
填料/增强材料玻璃纤维增强材料, 15% 填料按重量
添加剂热稳定剂
特性刚性,良好良好的强度耐化学性良好耐碳氢化合物耐油性能耐油脂性能热稳定性
用途安全帽齿轮垫圈高温应用汽车领域的应用
机构评级EC 1907/2006 (REACH)
RoHS 合规性RoHS 合规
外观可用颜色
形式粒子
加工方法注射成型
多点数据Isothermal Stress vs. Strain (ISO 11403-1)Secant Modulus vs.Strain (ISO 11403-1)Viscosity vs. Shear Rate (ISO 11403-2)
物理性能干燥调节后的单位制测试方法
比重1.23--g/cm³ASTM D792, ISO 1183
收缩率 - 流动 (3.18 mm)0.50--%
吸水率
24 hr1.4--%ASTM D570
23°C, 24 hr1.4--%ISO 62
饱和8.1--%ASTM D570
饱和, 23°C8.1--%ISO 62
平衡, 50% RH2.3--%ASTM D570
平衡, 23°C, 50% RH2.3--%ISO 62
硬度干燥调节后的单位制测试方法
洛氏硬度 (R 级)121--ASTM D785
机械性能干燥调节后的单位制测试方法
拉伸模量ISO 527-2
-40°C59506600MPaISO 527-2
23°C59602640MPaISO 527-2
80°C24702300MPaISO 527-2
121°C20901900MPaISO 527-2
抗张强度
断裂, -40°C160170MPaASTM D638, ISO 527-2
断裂, 23°C14079.0MPaASTM D638
断裂, 80°C60.020.0MPaASTM D638, ISO 527-2
断裂, 121°C50.040.0MPaASTM D638, ISO 527-2
断裂, 23°C14080.0MPaISO 527-2
伸长率
断裂, -40°C3.04.0%ASTM D638
断裂, 23°C4.09.0%ASTM D638, ISO 527-2
断裂, 80°C8.015%ASTM D638
断裂, 121°C7.06.0%ASTM D638
弯曲模量
-40°C58606430MPaASTM D790
23°C53102400MPaASTM D790
65°C2400--MPaASTM D790
121°C1930--MPaASTM D790
23°C47702210MPaISO 178
弯曲强度
-40°C214219MPaASTM D790
23°C172101MPaASTM D790
65°C110--MPaASTM D790
90°C90.0--MPaASTM D790
121°C76.0--MPaASTM D790
23°C16065.0MPaISO 178
冲击性能干燥调节后的单位制测试方法
简支梁缺口冲击强度ISO 179
-30°C5.5--kJ/m²ISO 179
23°C6.5--kJ/m²ISO 179
简支梁无缺口冲击强度 (23°C)40--kJ/m²ISO 179
悬壁梁缺口冲击强度
23°C59--J/mASTM D256
23°C5.0--kJ/m²ISO 180
热性能干燥调节后的单位制测试方法
热变形温度
0.45 MPa, 未退火217--°CISO 75-2/B
1.8 MPa, 未退火200--°CASTM D648
1.8 MPa, 未退火195--°CISO 75-2/A
熔融峰值温度220--°CASTM D3418, ISO 3146
线形热膨胀系数
流动5.0E-5--cm/cm/°CASTM E831
流动3.9E-5--cm/cm/°C
横向7.8E-5--cm/cm/°C
RTI ElecUL 746
0.800 mm130--°CUL 746
1.50 mm130--°CUL 746
3.00 mm130--°CUL 746
6.00 mm130--°CUL 746
RTI ImpUL 746
0.800 mm95.0--°CUL 746
1.50 mm105--°CUL 746
3.00 mm105--°CUL 746
6.00 mm105--°CUL 746
RTIUL 746
0.800 mm105--°CUL 746
电气性能干燥调节后的单位制测试方法
体积电阻率
1.50 mm> 1.0E+13--ohms·cmASTM D257
--> 1.0E+13--ohms·cmIEC 60093
介电强度40--kV/mmIEC 60243-1
介电常数IEC 60250
100 Hz3.60--IEC 60250
1 MHz3.40--IEC 60250
耗散因数IEC 60250
100 Hz0.010--IEC 60250
1 MHz0.020--IEC 60250
可燃性干燥调节后的单位制测试方法
UL 阻燃等级UL 94
0.800 mmHB--UL 94
1.50 mmHB--UL 94
3.00 mmHB--UL 94
6.00 mmV-2--UL 94
注射干燥单位制
干燥温度80.0°C
干燥时间2.0 到 4.0hr
建议的大水分含量0.15%
加工(熔体)温度250 到 290°C
模具温度80.0 到 95.0°C
注塑压力3.50 到 12.5MPa
注射速度快速
【优点】:
1.具高抗张强度;耐韧、耐冲击性特优
2.自润性、耐磨性佳、耐药品性优;
3.低温特性佳 具自熄性
【用途】:
电子电器:连接器、卷线轴、计时器、护盖断路器、开关壳座
汽车: 散热风扇、门把、油箱盖、进气隔栅、水箱护盖、灯座
工业零件:椅座、自行车输框、溜冰鞋底座、纺织梭、踏板、滑输
分类:防静电PA,导电PA,加纤防火PA,防火PA,抗紫外线耐候PA,高温挤出级PA。
PA6 尼龙 PA玻纤; 玻纤增强尼龙66 玻纤增强尼龙;玻纤增强尼龙6
【包装说明】:原厂原包(25kg/包)
【小订量】:25kg/包
【随货提供】: 原料物性表,SGS、ROHS、UL黄卡、MSDS、FDA、COA、PDF物性表等各项数据.