Zytel®101F NC010
尼龙树脂
杜邦高性能聚合物
产品描述:
未增强,聚酰胺66
Physical Properties物理性质
Metric公制数据
English英制数据
Comments测试方法
Specific Gravity比重
1.14 g/cc
DAM; ASTM D792
Water Absorption吸水率
1.2 %
@Temperature 23.0°C
1.2 %
@Temperature 73.4°F
Immersion 24h; DAM; ASTM D570
2.6 %
@Temperature 23.0°C
2.6 %
@Temperature 73.4°F
Equilibrium 50%RH; DAM; ISO 62, Similar to
8.5 %
@Temperature 23.0°C
8.5 %
@Temperature 73.4°F
Saturation, immersed; DAM; ISO 62, Similar to
Viscosity粘度
15000 cP
@ShearRate 7000 1/s,
Temperature 315°C
15000 cP
@ShearRate 7000 1/s,
Temperature 599°F
DAM; ISO 11443
109000 cP
@ShearRate 500 1/s,
Temperature 275°C
109000 cP
@ShearRate 500 1/s,
Temperature 527°F
Linear Mold Shrinkage线性收缩率
0.015 cm/cm
@Thickness3.20 mm
0.015 in/in
@Thickness0.126 in
Flow; DAM
Linear Mold Shrinkage,Flow线性收缩率/流动
0.014 cm/cm
@Thickness2.00 mm
0.014 in/in
@Thickness0.0787 in
Parallel; DAM; ISO 294-4
Mechanical Properties力学性能
Hardness, RockwellM罗氏硬度M
71
DAM; ASTM D785
Hardness, RockwellR罗氏硬度R
113
113
Tensile Strength拉伸强度
64.0 MPa
@Temperature23.0 °C
9280 psi
@Temperature73.4 °F
50%RH; ASTM D638
83.0 MPa
@Temperature23.0 °C
12000 psi
@Temperature73.4 °F
DAM; ASTM D638
Tensile Stress拉伸应力
0.000 MPa
@Strain0.000 %,
Temperature -40.0°C
0.000 psi
@Strain0.000 %,
Temperature -40.0°F
DAM; ISO 11403-1/-2
9.99 MPa
@Strain1.20 %,
Temperature 80.0 °C
1450 psi
@Strain1.20 %,
Temperature 176 °F
90.12 MPa
@Strain7.40 %,
Temperature 0.000°C
13070 psi
@Strain7.40 %,
Temperature 32.0 °F