| 密度 | 1.01 g/cc | 0.0365 lb/in³ | ASTM D792 |
| 吸水率 | 0.090 % | 0.090 % | ASTM D570 |
| 熔体流动速率 | 7.5 g/10 min @Load 5.00 kg, Temperature 200 °C | 7.5 g/10 min @Load 11.0 lb, Temperature 392 °F | ASTM D1238 |
| 肖氏硬度 (邵氏 D) | 65 | 65 | ASTM D2240 |
| 抗张强度(屈服) | 26.0 MPa | 3770 psi | 2 in per min; ASTM D638; Test specimens were injection moldedby ASTM D1897. |
| 伸长率 (断裂) | 160 % | 160 % | 2 in per min; ASTM D638; Test specimens were injection moldedby ASTM D1897. |
| 弯曲强度 | 34.0 MPa | 4930 psi | Test specimens were injection molded by ASTM D1897; ASTMD790 |
| 弯曲模量 | 1.413 GPa | 204.9 ksi | Test specimens were injection molded by ASTM D1897; ASTMD790 |
| 悬壁梁缺口冲击强度 | 0.410 J/cm @Thickness 3.17 mm | 0.768 ft-lb/in @Thickness 0.125 in | ASTM D256 |
| 冲击试验 | 29.7 J @Thickness 3.17 mm | 21.9 ft-lb @Thickness 0.125 in | Instrumented Total Energy; @ 150 in/sec impact rate; ASTMD3763 |
| 载荷下热变形温度(1.8 MPa) | 73.0 °C | 163 °F | ASTM D648 |
| 维卡软化温度 | 87.0 °C | 189 °F | ASTM D1525 |
| Transmission, Visible | 90 % | 90 % | ASTM D1003 |
| 加工温度 | <= 232 °C | <= 450 °F |