EVA 耐低温冲击 台湾台聚 UE659
EVA | UE631 | USIFE台湾聚合 | 透明 | VAC含量22% 熔脂1.4 | ||||||||
EVA | UE632 | VAC含量22% 熔脂2.2 | UE659 | VAC含量25% 熔脂2 | UE508 | VAC含量8% 熔脂85 | UE633 | VAC含量19% 熔脂20 | UE612-04 | VAC含量19% 熔脂150 | UE649-04 | VAC含量19% 熔脂400 |
产品参数
性能项目 | 试验条件[状态] | 测试方法 | 测试数据 | 数据单位 | ||
基本性能 | 熔体流动速率 | ASTM D-1238 | 2 | g/10min | ||
密度 | ASTM D-1505 | 0.947 | g/cm3 | |||
机械性能 | 硬度 | ASTM D-2240 | 31 | Shore D | ||
延展性 | 铸膜成型 | ASTM D-638(ASTM D-882) | 890 | % | ||
射出 | ASTM D-638(ASTM D-882) | 236 | % | |||
薄膜MD | ASTM D-638(ASTM D-882) | 290 | % | |||
薄膜TD | ASTM D-638(ASTM D-882) | 680 | % | |||
低温易脆性 | ASTM D-746 | <-76 | ℃/F50 | |||
冲击强度 | ASTM D-1709 | 444 | G/F50 | |||
降伏点抗张强度 | 铸膜成型 | ASTM D-638(ASTM D-882) | 212 | KG/cm2 | ||
射出 | ASTM D-638(ASTM D-882) | 114 | KG/cm2 | |||
薄膜MD | ASTM D-638(ASTM D-882) | 259 | KG/cm2 | |||
薄膜TD | ASTM D-638(ASTM D-882) | 240 | KG/cm2 | |||
热性能 | 熔点 | ASTM D-2117 | 77 | ℃ | ||
维卡软化点 | ASTM D-1525 | 54 | ℃ | |||
其它性能 | VA含量 | USIFE | 25 | % |