原包沙伯基础30GF增强PPE/PP NORYL PPX630F
备注说明 | 填料:玻璃纤维增强材料, 30% 填料按重量。 |
物理性能 | 比重 | ASTMD792 | 1.19 | g/cm³ | |
熔流率(熔体流动速率)(260°C/5.0kg) | ASTMD1238 | 2.6 | g/10min | ||
收缩率-流动(3.20mm) | InternalMethod | 0.20to0.23 | % | ||
MoldingShrinkage-AcrossFlow(3.20mm) | InternalMethod | 0.25to0.76 | % | ||
机械性能 | 抗张强度2(屈服) | ASTMD638 | 79.3 | MPa | |
抗张强度2(断裂) | ASTMD638 | 79.3 | MPa | ||
伸长率2(断裂) | ASTMD638 | 7.7 | % | ||
弯曲模量4(50.0mm跨距) | ASTMD790 | 5560 | MPa | ||
FlexuralStrength3(Break,50.0mmSpan) | ASTMD790 | 130 | MPa | ||
冲击性能 | 悬壁梁缺口冲击强度 | -30°C | ASTMD256 | 100 | J/m |
23°C | ASTMD256 | 170 | J/m | ||
悬壁梁缺口冲击强度(23°C) | ASTMD4812 | 830 | J/m | ||
装有测量仪表的落镖冲击 | -30°C,TotalEnergy | ASTMD3763 | 20.4 | J | |
23°C,TotalEnergy | ASTMD3763 | 19.1 | J | ||
热性能 | 载荷下热变形温度(0.45MPa,未退火,3.20mm) | ASTMD648 | 155 | °C | |
载荷下热变形温度(1.8MPa,未退火,3.20mm) | ASTMD648 | 134 | °C | ||
维卡软化温度 | ASTMD15254 | 162 | °C | ||
线形热膨胀系数-流动(-40到40°C) | ASTME831 | 1.4E-5 | cm/cm/°C | ||
线形热膨胀系数-横向(-40到40°C) | ASTME831 | 7.7E-5 | cm/cm/°C | ||
可燃性 | UL阻燃等级(1.5mm) | UL94 | HB |